Kimya ABS Kevlar

Kimya ABS Kevlar | 500g

48.50 €

IVA esclusa

Kimya ABS Kevlar Filament
The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibers.

prodotto presente su

Diametro

1.75 mm
2.85 mm

Disponibile

The Kimya ABS Kevlar 3D filament belongs to the styrenic polymer family. Acrylonitrile Butadiene Styrene Kevlar (ABS Kevlar) is a composite filament enriched in aramid fibers.

It offers properties that are superior to a standard ABS. It provides the printed parts with increased resistance to abrasion. It is used for finished parts and tools.

The Kimya ABS Kevlar 3D filament has the following properties:

Low warpage – compared to ABS-S-
Lighter-weight printed parts – compared to ABS Carbon-
Complies with the REACH standard

Riferimento PS1001TQ

Scarica

Kimya ABS Kevlar (TDS)

Scarica (579.04k)

Kimya ABS Kevlar (SDS)

Scarica (347.65k)

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.036 g/cm3
Moisture rate	INS-6711	< 0.5 %
Melt flow index (MFI)	ISO 1133-1 (@220°C – 10 kg)	35 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min - 20-220°C)	100 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XY
Printing Speed	40-70 mm/s
Infill	100% - rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	250-270°C
Bed T°	90-110°C

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	2,188 MPa
	Tensile Strength	ISO 527-2/5A/50	30 MPa
	Tensile strain at strength	ISO 527-2/1A/50	1.8 %
	Tensile Stress at Break	ISO 527-2/5A/50	27.3 MPa
	Tensile strain at break	ISO 527-2/5A/50	3.5 %
	Flexural modulus	ISO 178	1,662 MPa
	Flexural strength*	ISO 178	> 4,4 %
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	44.9 MPa
	Charpy impact resistance	ISO 179-1/1eA	5.1 kJ/m²
	Shore Hardness	ISO 868	70,1D

Note 1	*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2	The data should be considered as indicative values - Properties can be influenced by production conditions.

Created on 13/02/2018 - Revised on 01/07/2019.