Kimya TPU-R

29.95 €
IVA esclusa
paga in 3 rate con Klarna
pay in 3 with Klarna
paga en 3 plazos con Klarna
payez en 3 fois avec Klarna
prodotto presente su  Crea3D è presente su MEPA
Colore
Peso
Diametro
Disponibile

The Kimya TPU-R 3D filament belongs to the polyurethane family. Thermoplastic “-R” polyurethane (TPU-R) is formulated using recycled materials. It is a translucent filament with good elasticity. Furthermore, it offers a Shore hardness of 90A. It is used to print resistant and flexible parts. The Kimya TPU-R 3D filament is used in the electronics, automotive and consumer goods sectors. It offers the following properties:

  • Flexible
  • 100% made from recycled materials
  • Complies with the REACH regulation and the RoHS directive
PE2018TQ
PROPERTIESTEST METHODSVALUES
Diameter INS-6712 1.75 ± 0.1 mm
Density ISO 1183-1 1.14 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@200°C – 5 kg) 42 - 45 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 90-190°C) -33 °C

 

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

 

PRINTING DIRECTIONXY
Printing Speed 33 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 210°C
Bed T° 85°C

 

PRINTED SPECIMENS PROPERTIES

 

PROPERTIESTEST METHODSVALUES
MECHANICAL PROPERTIES Tensile modulus ISO 37/2/500 55.2 MPa
Tensile Strength ISO 37/2/500 27.7 MPa
Tensile strain at strength ISO 37/2/500 > 300 %
Tensile Stress at Break ISO 37/2/500 27.4 MPa
Tensile strain at break (type A) ISO 37/2/500 > 300 %
Flexural modulus ISO 178 46.6 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 1.9 MPa
Charpy impact resistance ISO 180 No Break
Shore Hardness ISO 868 90A
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.

Created on 17/12/2019 - Revised on 16/06/2022.