Kimya PETG-R
Kimya PETG-R (“-R for recycled”) 3D filament is formulated using materials from the industrial waste of a luxury and medical packaging products company. It is recycled and has comparable technical properties to our PETG-S (“-S for standard”) filament.
The Kimya PETG-R recycled 3D filament has the following properties:
- Contains at least 95% post-industrial recycled materials for the non-translucent colored version (100% for the translucent natural version)*
- Mechanical properties similar to PETG-S
- Odorless
- Easy to print
- 100% French recycled material
PROPERTIES | TEST METHODS | VALUES |
---|---|---|
Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
Density | ISO 1183-1 | 1.27 g/cm3 |
Melt flow index (MFI) | ISO 1133-1 (@225°C – 2.16 kg) | 9.2 g/10min |
Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 80 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
PRINTING DIRECTION | XY |
---|---|
Printing Speed | 30 mm/s |
Infill | 100% - rectilinear |
Infill Angle | 0°/0° |
Nozzle Temperature | 245°C |
Bed T° | 80°C |
PRINTED SPECIMENS PROPERTIES
PROPERTIES | TEST METHODS | VALUES | |
---|---|---|---|
MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/1A/50 | 1,845 MPa |
Tensile Strength | ISO 527-2/1A/50 | 47.1 MPa | |
Tensile strain at strength | ISO 527-2/1A/50 | 3.8 % | |
Tensile Stress at Break | ISO 527-2/1A/50 | 37.2 MPa | |
Tensile strain at break (type A) | ISO 527-2/5A/50 | 3.6-13 % | |
Flexural modulus | ISO 178 | 1,746 MPa | |
Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 60.8 MPa | |
Charpy impact resistance | ISO 179-1/1eA | 6.1 kJ/m² | |
Shore Hardness | ISO 868 | 75.5D |
Revised on 16/05/2022.