Kimya PA6-CO Filament
The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior.
fai acquisti fino a 3.000€ e paga in 3 rate con 
buy up to €3.000 and pay in 3 with
compra hasta 3.000€ y paga en 3 plazos con
achetez jusqu'à 3.000€ et payez en 3 fois avec
prodotto presente su 
The Kimya PA6-CO filament is a co-polymer based on a Nylon 6 grade. This unfilled polyamide has excellent tensile strength and very low warping behavior. Unlike other polyamide filaments on the market the PA6-CO is very easy to print and can be used seamlessly on open chamber 3D printers. It is the perfect standard polyamide go-to thanks to its inherent polyamide properties of high mechanical, chemical and heat resistance. Due to the general moisture sensitivity of polyamides, the filament must be dried before printing.
- Excellent printability even on open chamber printers
- Low warping
- Good wear resistance
Store away from light, humidity and heat to maintain the properties of the product.
PA2003TQ
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.157 g/cm3 |
| Melt flow index (MFI) | ISO 1133-1 (@240°C – 5 kg) | 24 - 28 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 20-300°C) | 65 °C |
| Melting Temperature (Tm) | ISO 11357-1 DSC (10°C/min – 20-300°C) | 227 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 55 mm/s |
| Infill | 100% - rectilinear |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 270°C |
| Bed T° | 75°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/5A/50 | 2,166 MPa |
| Tensile Strength | ISO 527-2/5A/50 | 56.1 MPa | |
| Tensile strain at strength | ISO 527-2/5A/50 | 4,3 % | |
| Tensile Stress at Break | ISO 527-2/5A/50 | 13.4 MPa | |
| Tensile strain at break (type A) | ISO 527-2/5A/50 | 16.2 % | |
| Flexural modulus | ISO 178 | 2,017 MPa | |
| Deformation at Flexural Strain | ISO 178 | <5 td=""> | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 65.9 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 3.9 kJ/m² | |
| Shore Hardness | ISO 868 | 77,3 |
Revised on 16/06/2022.