Kimya PPSU-S | 500g
173.00 €
Tax excluded
Not Rated
Kimya PPS-U Filament
The Kimya PPSU-S 3D filament belongs to the polysulfone family. Polyphenylsulfone (PPSU) is an amorphous thermoplastic. It is a technical material with an elevated glass transition temperature and low humidity absorption.
prodotto presente su 
The Kimya PPSU-S 3D filament belongs to the polysulfone family. Polyphenylsulfone (PPSU) is an amorphous thermoplastic. It is a technical material with an elevated glass transition temperature and low humidity absorption. It benefits from good chemical and thermal resistance. PPSU-S can be used in multiple sectors, notably low-volume injection molds, automotive spare parts, chemical treatment, oil and gas… The Kimya PPSU-S 3D filament has the following properties:
- High temperature resistance
- Hydrolysis resistance
- Flame retardant – eligible to UL94 V0
- Aerospace FAR 25.853 Standard
- Food contact under EU 10/2011
- Complies with the REACH regulation and the RoHS directive
Store away from light, humidity and heat to maintain the properties of the product.
PY1001TQ
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm |
| Density | ISO 1183-1 | 1.3 g/cm3 |
| Melt flow index (MFI) | ISO 1133-1 (@365°C – 5 kg) | 16 - 21 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 0-420°C) | 224 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 35 mm/s |
| Infill | 100% - |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 380°C |
| Bed T° | 220°C |
| Chamber T° | 220°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| THERMAL PROPERTIES | Maximum use T° | - | 176 °C |
| Heat distortion temperature (HDT) (0,45Mpa) | ASTM D648 | °C | |
| Heat distortion temperature (HDT) (1,8Mpa) | ASTM D648 | 207 °C | |
| ELECTRICAL PROPERTIES | Volume resistivity | ASTM D257 | 9.0*1015 Ω/sq |
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527-2/1A/50 | 1,752 MPa |
| Tensile Strength | ISO 527-2/1A/50 | 53.8 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 6,4 % | |
| Tensile Stress at Break | ISO 527-2/1A/50 | 53.8 MPa | |
| Tensile strain at break (type A) | ISO 527-2/1A/50 | 6,4 % | |
| Flexural modulus | ISO 178 | 1,664 MPa | |
| Deformation at Flexural Strain | ISO 178 | 5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 54.1 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 20.7 kJ/m² | |
| Shore Hardness | ISO 868 | 79,8D |
| Note 1 | *According to ISO 178, end of the test at 5% deformation even if there is no specimen break. |
| Note 2 | The data should be considered as indicative values - Properties can be influenced by production conditions. |
Created on 24/09/2019 - Revised on 13/03/2023.