Kimya PEI-1010 (ULTEM®)
135.00 €
Tax excluded
Not Rated
Kimya PEI-1010
The Kimya PEI-1010 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. It benefits from good resistance to temperature and solvents, as well as high dimensional stability.
fai acquisti fino a 3.000€ e paga in 3 rate con 
buy up to €3.000 and pay in 3 with
prodotto presente su 
The Kimya PEI-1010 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. It benefits from good resistance to temperature and solvents, as well as high dimensional stability. It is used in the electronics, transport and medical sectors. The Kimya PEI-1010 3D filament is based on ULTEM by Sabic® and it has the following properties:
- High rigidity
- UV resistance
- Flame retardant – UL94 V0 eligible
- Food contact certification EU 10/2011, FDA 21 CFR
- Complies with the REACH regulation and the RoHS directive
Store away from light, humidity and heat to maintain the properties of the product.
PI1001TQ
FILAMENT PROPERTIES
| PROPERTIES | TEST METHODS | VALUES |
|---|---|---|
| Diameter | INS-6712 | 1.75 ± 0.1 mm 2.85 ± 0.1 mm |
| Density | ISO 1183-1 | 1.28 g/cm3 |
| Melt flow index (MFI) | ISO 1133-1 (@340°C – 5 kg) | 14 - 16 g/10min |
| Glass transition temperature (Tg) | ISO 11357-1 DSC (10°C/min - 0-420°C) | 217 °C |
PRINT PARAMETERS AND SPECIMENS DIMENSIONS
| PRINTING DIRECTION | XY |
|---|---|
| Printing Speed | 40 mm/s |
| Infill | 100% - |
| Infill Angle | 45°/-45° |
| Nozzle Temperature | 380°C |
| Chamber T° | 220°C |
PRINTED SPECIMENS PROPERTIES
| PROPERTIES | TEST METHODS | VALUES | |
|---|---|---|---|
| MECHANICAL PROPERTIES | Tensile modulus | ISO 527 | 2,917.5 MPa |
| Tensile Strength | ISO 527-2/1A/50 | 90.9 MPa | |
| Tensile strain at strength | ISO 527-2/1A/50 | 5,6 % | |
| Tensile Stress at Break | ISO 527-2/1A/50 | 90.9 MPa | |
| Tensile strain at break (type A) | ISO 527-2/1A/50 | 5,6 % | |
| Tensile strain at break (type B et C) | ISO 527-2/1A/50 | 5.6 % | |
| Flexural modulus | ISO 178 | 2,236 MPa | |
| Deformation at Flexural Strain | ISO 178 | >5 % | |
| Flexural stress at conventional deflection (3,5% strain)* | ISO 178 | 76 MPa | |
| Charpy impact resistance | ISO 179-1/1eA | 3.1 kJ/m² | |
| Shore Hardness | ISO 868 | 84,5D |
| Note 1 | The data should be considered as indicative values - Properties can be influenced by production conditions. |
Created on 10/03/2022 - Revised on 13/03/2023.
You might also like
Customers who bought this product also bought:
Kimya PEI-1010
The Kimya PEI-1010 3D filament belongs to the family of thermoplastic polyimides. Polyetherimide (PEI) is an amorphous thermoplastic. It benefits from good resistance to temperature and solvents, as well as high dimensional stability.
No customer reviews for the moment.