Chiusura uffici e magazzino dal 24 Dicembre al 06 Gennaio. Gli ordini effettuati in queste date verranno elaborati a partire dal 07 Gennaio 2025.

PROMOZIONI attive  Italiano  Filamenti KIMYA  |  Bambu Lab X1E Bundle  |  Stampanti 3D UltiMaker e Raise3D

Offices and warehouse closure from December 24th to January 6th. Orders placed on these dates will be processed starting from 07 January 2025.

Active PROMOTIONS  English  KIMYA Filaments  |  Bambu Lab X1E Bundle  |  UltiMaker and Raise3D 3D printers

Cierre de oficinas y depósitos del 24 de Diciembre al 6 de Enero. Los pedidos realizados en estas fechas se procesarán a partir del 7 de enero de 2025..

PROMOCIONES activas  Español  Filamentos KIMYA  |  Bambu Lab X1E Bundle  |  Impresoras 3D UltiMaker y Raise3D

Fermeture des bureaux et de l'entrepôt du 24 Décembre au 6 Janvier. Les commandes passées à ces dates seront traitées à partir du 7 Janvier 2025.

PROMOTIONS actives  Français  Filaments KIMYA  |  Bambu Lab X1E Bundle  |  Imprimantes 3D UltiMaker et Raise3D

Schließung von Büro und Lagerhalle vom 24. Dezember bis 6. Januar. An diesen Terminen aufgegebene Bestellungen werden ab dem 7. Januar 2025 bearbeitet.

Aktive WERBEAKTIONEN  Deutsch  KIMYA-Filamente  |  Bambu Lab X1E Bundle  |  UltiMaker und Raise3D 3D-Drucker

Addigy® PA6/66-GF20 FR LS | 2.85mm | 1Kg

212.00 €
Tax excluded
Not Rated
Add Review
paga in 3 rate con Klarna
pay in 3 with Klarna
paga en 3 plazos con Klarna
payez en 3 fois avec Klarna
Zahlen Sie in 3 Raten mit Klarna
prodotto presente su  Crea3D è presente su MEPA
There are not enough products in stock


Addigy® PA6/66-GF20 FR LS is a newly developed flame retardant material that is compliant with EN 45545-2, NFPA 130 (ASTM E162, ASTM E662) and SMP 800-C. This material was designed specifically for 3D printing to achieve ideal mechanical properties with excellent flame retardancy, low smoke and low toxicity. The material is ideal for the production of end use parts using printers with enclosed or heated chambers.

Benefits
  • Flame retardant material
  • Semi-crystalline thermoplastic
  • Good impact strength and stiffness
  • Good low temperature properties (e.g. -40°C)
  • Outstanding wear resistance
  • Good temperature resistance
  • Reduced thermo-oxidative degradation
  • Improved long term heat and stability to ultraviolet and visible light

Applications*
  • Functional end use parts
  • Functional prototypes
*Subject to detailed product specifications.

Color
  • Black

Printing Parameters

  • Print Temperature = 230-250°C
  • Print Speed = 20-50 mm/s
  • Bed Adhesion = Magigoo PA
  • Bed Temperature = 80°C
  • Fan Settings = off to low
  • Nozzle = use of a fiber capable nozzle (e.g. hardened steel, ruby)
16136297
Property  Typical Values Units Test Method Test Specimen
   black natural       
MECHANICAL PROPERTIES          
Tensile stress at yield, 50 mm/min     MPa ISO 527 Injection molded
    -- MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   -- MPa ISO 527 3D printed XY / flat at 240°C
    -- MPa ISO 527 3D printed XZ / on edge at 235°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Tensile stress at break, 50 mm/min     MPa ISO 527 Injection molded
  46 MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   52 MPa ISO 527 3D printed XY / flat at 240°C
    53 MPa ISO 527 3D printed XZ / on edge at 235°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Tensile elongation at yield, 50 mm/min   -- % ISO 527 3D printed XY / flat at 240°C
at -40°C   -- % ISO 527 3D printed XY / flat at 240°C
    -- % ISO 527 3D printed XZ / on edge at 240°C
      % ISO 527 3D printed ZX / upright at 240°C
Tensile elongation at break, 50 mm/min     % ISO 527 Injection molded
    2.5 % ISO 527 3D printed XY / flat at 240°C
at -40°C   2.1 % ISO 527 3D printed XY / flat at 240°C
    1.7 % ISO 527 3D printed XZ / on edge at 240°C
    % ISO 527 3D printed ZX / upright at 235°C
Tensile modulus (modulus of elasticity), 1 mm/min     MPa ISO 527 Injection molded
  3999 MPa ISO 527 3D printed XY / flat at 240°C
at -40°C   4056 MPa ISO 527 3D printed XY / flat at 240°C
    4876 MPa ISO 527 3D printed XZ / on edge at 240°C
      MPa ISO 527 3D printed ZX / upright at 235°C
Flexural modulus   5588 MPa ISO 178 Injection molded
Flexural strength   147 MPa ISO 178 Injection molded
Izod impact notched     MPa ISO 180 Injection molded
Charpy impact notched     MPa ISO 179 Injection molded
  13.1 MPa ISO 179 3D printed XY / flat at 240°C
FLAMMABILITY PROPERTIES        
UL 94 flammability rating V-2 at 0.4 mm V-2 at 0.4 mm UL 94 3D printed XY / flat at 240°C
  V-2 at 0.8 mm  V-2 at 0.8 mm UL 94 3D printed XY / flat at 240°C
  V-1 at 1.6 mm  V-2 at 1.6 mm UL 94 3D printed XY / flat at 240°C
   V-1 at 2.0 mm UL 94 3D printed XY / flat at 240°C
  V-0 at 3.2 mm V-0 at 3.2 mm UL 94 3D printed XY / flat at 240°C
EN 45545-2+A1 NORM      
Oxygen index   33.6 at 4 mm % R22 - EN ISO 4589-2 3D printed XY / flat at 240°C
Smoke production (Ds max)   111.1 at 4 mm R22 - EN ISO 5659-2, 25 kW/m2 3D printed XY / flat at 240°C
ITCPNL   0.51 at 4 mm NF X 70-100-1, NF X 70-100-2, 600°C 3D printed XY / flat at 240°C
      3D printed XY / flat at 240°C
      3D printed XY / flat at 240°C
NFPA 130 NORM          
Radiant panel index (Is)   8 at 6 mm   ASTM  E162-15b 3D printed XY / flat at 240°C
Optical density at 4 minutes (Ds)   94 at 6 mm   ASTM E662-18 3D printed XY / flat at 240°C
        3D printed XY / flat at 240°C
Toxic gas generation   pass   Bombardier SMP 800-C 3D printed XY / flat at 240°C
FAR 25.853 NORM          

Burn length

   20.3 (0.8) mm (") Vertical test – 12 seconds, FAR 25.853 3D printed XY / flat at 240°C

Flame time

   6.1 s

Vertical test – 12 seconds, FAR 25.853

 3D printed XY / flat at 240°C

Flaming time of drippings

   0.0 s Vertical test – 12 seconds, FAR 25.853 3D printed XY / flat at 240°C

Burn rate

   n/a (< 38.1 ( 1.5)) mm/min (in/min) Horizontal test – 12 seconds, FAR 25.85 3D printed XY / flat at 240°C
THERMAL PROPERTIES          
Melting point   195 °C ISO 11357, DSCb  
Glass transition temperature   °C ISO 11357, DSCb  
Heat deflection temperature at 1.8 MPa (A)     °C ISO 75 Injection molded
    114 °C ISO 75 3D printed XY / flat at 240°C
Heat deflection temperature at 0.45 MPa (B)     °C ISO 75 Injection molded
    168 °C ISO 75 3D printed XY / flat at 240°C
GENERAL PROPERTIES          
Density   1293 kg/m3 ISO 1183  
pH 4.3 4.5     1% in H2O
Water absorption     % ISO 62 24 hours at 23°C
Water content - coulometric Karl Fischer     μg/g ISO 12937  
Water content   %
 ISO 15512 after drying at 120°C for 2 hours
non-volatile-matter content   ~30 % ISO 3251  