Promozioni attive  Italiano  Filamenti KIMYA -25%  |  Bambu Lab X1E Carbon Speed Bundle  |  Scanner 3D manuali Shining3D

Active Promotions  English  KIMYA Filaments -25%  |  Bambu Lab X1E Carbon Speed Bundle  |  Shining3D Handheld 3D scanners

Promociones activas  Español  Filamentos KIMYA -25%  |  Bambu Lab X1E Carbon Speed Bundle  |  Escáneres 3D manuales Shining3D

Promotions actives  Français  Filaments KIMYA -25%  |  Bambu Lab X1E Carbon Speed Bundle  |  Scanners 3D manuels Shining3D

Aktive Werbeaktionen  Deutsch  KIMYA-Filamente -25%  |  Bambu Lab X1E Carbon Speed Bundle  |  Shining3D-Handscanner

Bambu PLA Aero | 1.75mm | 1Kg

40.33 €
Tax excluded
Not Rated
paga in 3 rate con Klarna
pay in 3 with Klarna
paga en 3 plazos con Klarna
payez en 3 fois avec Klarna
Zahlen Sie in 3 Raten mit Klarna
prodotto presente su  Crea3D è presente su MEPA
Color
Weight

Volume discounts

QuantityPriceYou Save
438.31 €Up to 8.07 €
836.30 €Up to 32.26 €
1234.28 €Up to 72.59 €
There are not enough products in stock


Bambu PLA Aero

Bambu PLA Aero achieves low density and light weight by foaming at high temperatures during printing and creating small holes inside the prints. It's the perfect choice for light-weight and energy-saving prints, including unmanned aerial vehicles (UAVs), aerodynamic models, and gliders.

Foaming PLA materials (PLA Aero) have high requirements for material drying and parameter settings. Please carefully read Instructions for printing aircraft model with foaming PLA (PLA Aero) before starting the printing process.

 

 

Low Density and Light Weight

Bambu PLA Aero has almost the same filament density as regular PLA, while the prints density is only 50% to 80%.


* When printing models of the same volume, PLA Aero is about half the weight of PLA Basic.

 

Controllable Model Density

Achieve lower density of the prints by increasing printing temperature and lowering flow rate.


* The average density of prints will vary with changes in parameters such as actual printing temperature, flow rate ratio, printing speed, model size, wall thickness and infill density.

 

Parameter Setting Average Density
Printing Temperature Increases ↗ Decreases ↘
Printing Speed Increases ↗ Stable or Increases ↗
Flow Rate Ratio Increases ↗ Increases ↗
Model Size Increases ↗ Decreases ↘
Wall Thickness(Wall loops) Increases ↗ Increases ↗
Infill Density Increases ↗ Increases ↗

 

The relationship between the maximum foaming rate, minimum print density, and printing temperature of PLA Aero.

Printing Temperature
Minimum Flow Rate Ratio
Maximum Volumetric Expansion Ratio
Maximum Foaming Rate
Minimum Prints Density
190 °C ~ 0.95 ~ 100% ~ 0% ~ 1.17 g/cm³
200 °C 0.89 110% 10% 1.06 g/cm³
210 °C 0.85 115% 15% 1.02 g/cm³
220 °C 0.76 129% 29% 0.91 g/cm³
230 °C 0.62 158% 58% 0.74 g/cm³
240 °C 0.45 217% 117% 0.54 g/cm³
250 °C 0.38 258% 158% 0.45 g/cm³
260 °C 0.35 280% 180% 0.42 g/cm³
270 °C 0.37 265% 165% 0.44 g/cm³


Specimen Test: Nozzle Type: 0.4 mm; Printing Speed: 80 mm/s; Model size (L*W*H): 80*10*4 mm³ (the XY direction).
The actual required flow rate ratio and final model density may vary with different models.

 

Matte Finish For Easy Coloring

Bambu PLA Aero provides an easy-to-color matte surface texture with better dyeing results as compared to PLA Basic.

 

 

RFID for Intelligent Printing

All printing parameters are embedded in RFID, which can be read through our AMS (Automatic Material System). Load and print! No more tedious setting steps.

 

A11-K0-1.75-1000-SPL

Download


Recommended Printing Settings
Drying Settings (Blast Drying Oven) 55 °C,8 h
Printing and Keeping Container's Humidity < 20% RH (Sealed, with Desiccant)
Nozzle Temperature 210 - 260 °C
Bed Temperature (with Glue) 35 - 45 °C
Printing Speed < 180 mm/s

 

Physical Properties
Density 1.21 g/cm³
Vicat Softening Temperature 54 °C
Heat Deflection Temperature 53 °C
Melting Temperature 153 °C
Melt Index 7.7 ± 0.6 g/10 min

 

Mechanical Properties
Tensile Strength 24 ± 2 MPa
Breaking Elongation Rate 2.6 ± 0.7 %
Bending Modulus 1690 ± 120 MPa
Bending Strength 45 ± 4 MPa
Impact Strength 28.8 ± 1.3 kJ/m²